Super Hydrophobic Material OR-112(Series)
> Material Name : OR-112
> Size : 18Φmm X 7t mm (Crucible)
> Size : 12Φmm X 4t mm (Ceramic pill)
> Size : 17Φmm X 7t mm (SUS beads)
> Size : 15Φmm X 7t mm (SUS beads)
> Size : 13Φmm X 6t mm (SUS beads)
Experimental Condition
· Coating Machine : Univac 1350
· Evaporation Source : Mo Ring type
· Substrate : CR-39 with (SiO2 is coated on CR-39 substrate)
· Distance from source to substrate (mm) : 880mm
· Substrate temperature (℃) : 60℃
· Start pressure (Torr) : 3.5X10 Torr
· Evaporation Source : Resistance heating(figure 1 / Indirect heating system)
Deposition / Principle Graph
The information herein is considered to be a fair representation of this product.
The data are not to be interepretered as a specification or guarantee of properties.
Eurama Corporation makes no inplied warranties as to its accuracy and assumes no liability arising Out of its use by others.
The information does not constitute a license to use or infringe any patents.
※ Please contact us to obtain MSDS.
Nomal Hydrophobic WR-110
> Material Name : WR-110
> R Type Size : 8Φmm X 5t mm
> S Type Size : 10Φmm X 6t mm
Application
WR-110 is designed to repel any water drop on the surface of organic lens and keep the surface clean, and help easy to clean if any contamination.
Experimental Condition
WR-110, water repellent top coating material, protects the AR layer deposited on the organic substrates used by its super hydrophobic and lubricative property. The thin film coated with WR-110 have anti-soiling and water repellent property, and are easy to clean stains if any. Also, it has excellent abrasion resistance due to its lubricative property.
Deposition Rate
Properties
ⓐ Water repellent property : Slide angle 18.4º
ⓑ Abrasion resistance test : Core Tech CT-RB1
Test condition – load : 5g
cycle : 10,000
Destruction of AR coated film is observed by UV spectroscopy after the abrasion resistance test. The reflectance of film becomes higher with the increasing destruction of AR layer caused by abrasion to the coatings.
WR-110 is the best top coating material for the protection of AR layer deposited on the organic lenses.
Storage
– Keep away from direct sunlight and high humidity.
– Storage temperature should not exceed 50℃.
– WR-110 can be stored up to one year at the room temperature.
Precaution
WR-110 may be broken by a strong mechanic shock.
※ Please contact us to obtain MSDS.
Super Hydrophobic Material OR-112(Series)
> Material Name : OR-112
> Size : 18Φmm X 7t mm (Crucible)
> Size : 12Φmm X 4t mm (Ceramic pill)
> Size : 17Φmm X 7t mm (SUS beads)
> Size : 15Φmm X 7t mm (SUS beads)
> Size : 13Φmm X 6t mm (SUS beads)
Experimental Condition
· Coating Machine : Univac 1350
· Evaporation Source : Mo Ring type
· Substrate : CR-39 with (SiO2 is coated on CR-39 substrate)
· Distance from source to substrate (mm) : 880mm
· Substrate temperature (℃) : 60℃
· Start pressure (Torr) : 3.5X10 Torr
· Evaporation Source : Resistance heating(figure 1 / Indirect heating system)
Deposition / Principle Graph
The information herein is considered to be a fair representation of this product.
The data are not to be interepretered as a specification or guarantee of properties.
Eurama Corporation makes no inplied warranties as to its accuracy and assumes no liability arising Out of its use by others.
The information does not constitute a license to use or infringe any patents.
※ Please contact us to obtain MSDS.
Nomal Hydrophobic WR-110
> Material Name : WR-110
> R Type Size : 8Φmm X 5t mm
> S Type Size : 10Φmm X 6t mm
Application
WR-110 is designed to repel any water drop on the surface of organic lens and keep the surface clean, and help easy to clean if any contamination.
Experimental Condition
WR-110, water repellent top coating material, protects the AR layer deposited on the organic substrates used by its super hydrophobic and lubricative property. The thin film coated with WR-110 have anti-soiling and water repellent property, and are easy to clean stains if any. Also, it has excellent abrasion resistance due to its lubricative property.
Deposition Rate
Properties
ⓐ Water repellent property : Slide angle 18.4º
ⓑ Abrasion resistance test : Core Tech CT-RB1
Test condition – load : 5g
cycle : 10,000
Destruction of AR coated film is observed by UV spectroscopy after the abrasion resistance test. The reflectance of film becomes higher with the increasing destruction of AR layer caused by abrasion to the coatings.
WR-110 is the best top coating material for the protection of AR layer deposited on the organic lenses.
Storage
– Keep away from direct sunlight and high humidity.
– Storage temperature should not exceed 50℃.
– WR-110 can be stored up to one year at the room temperature.
Precaution
WR-110 may be broken by a strong mechanic shock.